Characterization and Failure Analysis of Plastics - read free eBook in online reader or directly download on the web page. Select files or add your book in reader. Download and read online ebook Characterization and Failure Analysis of Plastics write by ASM International. This book was released on 2003-01-01. Characterization and Failure Analysis of Plastics available in PDF, EPUB and Kindle. The selection and application of engineered materials is an integrated process that requires an understanding of the interaction between materials properties, manufacturing characteristics, design considerations, and the total life cycle of the product. This reference book on engineering plastics provides practical and comprehensive coverage on how the performance of plastics is characterized during design, property testing, and failure analysis. The fundamental structure and properties of plastics are reviewed for general reference, and detailed articles describe the important design factors, properties, and failure mechanisms of plastics. The effects of composition, processing, and structure are detailed in articles on the physical, chemical, thermal, and mechanical properties. Other articles cover failure mechanisms such as: crazing and fracture; impact loading; fatigue failure; wear failures, moisture related failure; organic chemical related failure; photolytic degradation; and microbial degradation. Characterization of plastics in failure analysis is described with additional articles on analysis of structure, surface analysis, and fractography.
Plastics Failure Guide
Plastics Failure Guide - read free eBook in online reader or directly download on the web page. Select files or add your book in reader. Download and read online ebook Plastics Failure Guide write by Myer Ezrin. This book was released on 2013. Plastics Failure Guide available in PDF, EPUB and Kindle. Plastics failure, to a certain extent, is the result of a phenomenal increase in the number and variety of applications in relatively few years. The focus of this book is on actual field and product failures. The treatment is comprehensive, emphasizing cause and prevention. The concept of the interdependence of material, design, and processing is applied to all examples and cases. The "how to" of prevention is brought out as a logical extension of the cause of failure.
Fractography in Failure Analysis of Polymers
Fractography in Failure Analysis of Polymers - read free eBook in online reader or directly download on the web page. Select files or add your book in reader. Download and read online ebook Fractography in Failure Analysis of Polymers write by Michael D. Hayes. This book was released on 2015-05-08. Fractography in Failure Analysis of Polymers available in PDF, EPUB and Kindle. Fractography in Failure Analysis of Polymers provides a practical guide to the science of fractography and its application in the failure analysis of plastic components. In addition to a brief background on the theory of fractography, the authors discuss the various fractographic tools and techniques used to identify key fracture characteristics. Case studies are included for a wide range of polymer types, applications, and failure modes, as well as best practice guidelines enabling engineers to apply these lessons to their own work. Detailed images and their appropriate context are presented for reference in failure investigations. This text is vital for engineers who must determine the root causes of failure when it occurs, helping them further study the ramifications of product liability claims, environmental concerns, and brand image. - Presents a comprehensive guide to applied fractography, enabling improved reliability and longevity of plastic parts and products - Includes case studies that demonstrate material selection decisions and how to reduce failure rates - Provides best practices on how to analyze the cause of material failures, along with guidelines on improving design and manufacturing decisions
Failure of Plastics and Rubber Products
Failure of Plastics and Rubber Products - read free eBook in online reader or directly download on the web page. Select files or add your book in reader. Download and read online ebook Failure of Plastics and Rubber Products write by D. Wright. This book was released on 2001-06. Failure of Plastics and Rubber Products available in PDF, EPUB and Kindle. Plastics and rubbers together make up the most adaptable and varied class of materials available to product designers. They may be transparent or opaque, rigid or flexible, lightweight, insulating, and weatherproof. They are used in almost every industry, and in every part of the home. Applications range from the humble hot water bottle to the sheathing on a high voltage cable, and from a simple scrubbing brush to a tank for storing hydrochloric acid. Products may be disposable (e.g. packaging goods) or intended to last for decades, such as a buried sewage pipe. However, it is this very diversity which makes materials selection so difficult, and appropriate design so important. Indeed the one thing that all these particular products have in common is their presence in this book of failures. Failures due to degradation may result from exposure to the weather or an aggressive operating environment. Alternatively they may be caused by the introduction of an external agent unforeseen by the product designer. They may be rapid or very slow, and they may result from a combination of factors. In this book Dr. Wright describes the following mechanisms of polymer degradation, and then illustrates each failure mechanism with a number of case studies: Thermo-oxidation, Photo-oxidation, Degradation due to ionising radiation, Chemical attack, Environmental stress cracking, Other miscellaneous effects, including treeing, electrochemical degradation and biodegradation. Many of the case studies are based on Dr. Wrights own experiences whilst working at Rapra. In each case he describes the circumstances of the failure, and discusses both the consequences of the failure and the lessons that may be learned from it. Most of the failed products are familiar to us all, and his style is both readable and informative. Photographs are included where available. The book will be essential reading for designers, engineers, product specifiers and forensic engineers. Materials suppliers and processors will also benefit from the pragmatic analysis and advice it contains. It will also be of value to all students of polymer science and technology, providing an essential insight into the practical application of plastics and rubbers and the potential problems. Finally, it will be of interest to a much broader readership, including anyone who ever wondered why things break, and it should become a standard reference work in all technical libraries. This book was written with the support of the UK Department of Trade and Industry. It is intended to raise awareness of the causes and consequences of polymer product failures, in order to reduce the future incidences of such failures, and their considerable costs to industry
Plastics Failure Analysis and Prevention
Plastics Failure Analysis and Prevention - read free eBook in online reader or directly download on the web page. Select files or add your book in reader. Download and read online ebook Plastics Failure Analysis and Prevention write by John Moalli. This book was released on 2001-12-31. Plastics Failure Analysis and Prevention available in PDF, EPUB and Kindle. This book contains analysis of reasons that cause products to fail. General methods of product failure evaluation give powerful tools in product improvement. Such methods, discussed in the book, include practical risk analysis, failure mode and effect analysis, preliminary hazard analysis, progressive failure analysis, fault tree analysis, mean time between failures, Wohler curves, finite element analysis, cohesive zone model, crack propagation kinetics, time-temperature collectives, quantitative characterization of fatigue damage, and fracture maps. Methods of failure analysis are critical to for material improvement and they are broadly discussed in this book. Fractography of plastics is relatively a new field which has many commonalities with fractography of metals. Here various aspects of fractography of plastics and metals are compared and contrasted. Fractography application in studies of static and cycling loading of ABS is also discussed. Other methods include SEM, SAXS, FTIR, DSC, DMA, GC/MS, optical microscopy, fatigue behavior, multiaxial stress, residual stress analysis, punch resistance, creep-rupture, impact, oxidative induction time, craze testing, defect analysis, fracture toughness, activation energy of degradation.Many references are given in this book to real products and real cases of their failure. The products discussed include office equipment, automotive compressed fuel gas system, pipes, polymer blends, blow molded parts, layered, cross-ply and continuous fiber composites, printed circuits, electronic packages, hip implants, blown and multilayered films, construction materials, component housings, brake cups, composite pressure vessels, swamp coolers, electrical cables, plumbing fittings, medical devices, medical packaging, strapping tapes, balloons, marine coatings, thermal switches, pressure relief membranes, pharmaceutical products, window profiles, and bone cements.